Resiflow P-71

Resiflow P-71 is based on a low viscosity liquid acrylic polymer that has been converted into free-flowing powder by adsorption onto silica-type filler. The product has superior flow and leveling characteristics with excellent clarity essential for clear powder coatings.

Surface defects such as orange peel, craters, pinholes, and other imperfections can be reduced or eliminated by incorporating 0.7-1.5% of Resiflow P-71 into powder coating formulations. It is especially recommended for use in GMA and TGIC clears. For best results, Resiflow P-71 should be dry-blended with other coating raw materials, then homogenized in a heated extruder. The active ingredient is released and homogenized with the other components during extrusion, which results in a uniform system.

As with any silica supported flow control agent, Resiflow P-71 should be thoroughly evaluated to determine the best processing method and the optimum concentration of the additive, suitability for the application, as well as to test compatibility and recoat adhesion.

Resiflow P-71 is based on a low viscosity liquid acrylic polymer that has been converted into free-flowing powder by adsorption onto silica-type filler. The product has superior flow and leveling characteristics with excellent clarity essential for clear powder coatings.

Surface defects such as orange peel, craters, pinholes, and other imperfections can be reduced or eliminated by incorporating 0.7-1.5% of Resiflow P-71 into powder coating formulations. It is especially recommended for use in GMA and TGIC clears. For best results, Resiflow P-71 should be dry-blended with other coating raw materials, then homogenized in a heated extruder. The active ingredient is released and homogenized with the other components during extrusion, which results in a uniform system.

As with any silica supported flow control agent, Resiflow P-71 should be thoroughly evaluated to determine the best processing method and the optimum concentration of the additive, suitability for the application, as well as to test compatibility and recoat adhesion.