Resiflow PL-200A

Surface defects such as orange peel, craters, pinholes, and other imperfections can be reduced or eliminated by incorporating 0.7-1.5% of Resiflow® PL-200A into pigmented powder coating formulations. It is not recommended for use in clears. For best results, Resiflow® PL-200A should be dry-blended with other coating raw materials, then homogenized in a heated extruder. The active ingredient is released and homogenized with the other components during extrusion, which results in a uniform system.

Resiflow® PL-200A is based on the liquid acrylic polymer product Resiflow® LV that has been converted into free-flowing powder by adsorption onto silica-type filler. This active ingredient is also available in a three different polyester masterbatches for powder coating formulations that require the flow control agent to be predispersed for optimal uniformity and for applications where silica supported additives may not be suitable.

As with any silica supported flow control agent, Resiflow® PL-200A should be thoroughly evaluated to determine the best processing method and the optimum concentration of the additive, suitability for the application, as well as to test compatibility and recoat adhesion.

Surface defects such as orange peel, craters, pinholes, and other imperfections can be reduced or eliminated by incorporating 0.7-1.5% of Resiflow® PL-200A into pigmented powder coating formulations. It is not recommended for use in clears. For best results, Resiflow® PL-200A should be dry-blended with other coating raw materials, then homogenized in a heated extruder. The active ingredient is released and homogenized with the other components during extrusion, which results in a uniform system.

Resiflow® PL-200A is based on the liquid acrylic polymer product Resiflow® LV that has been converted into free-flowing powder by adsorption onto silica-type filler. This active ingredient is also available in a three different polyester masterbatches for powder coating formulations that require the flow control agent to be predispersed for optimal uniformity and for applications where silica supported additives may not be suitable.

As with any silica supported flow control agent, Resiflow® PL-200A should be thoroughly evaluated to determine the best processing method and the optimum concentration of the additive, suitability for the application, as well as to test compatibility and recoat adhesion.